The Structure and Composite Materials Laboratory (SCML) can assume a wide range of experiments. From characterizing a material to testing its mechanical properties, the equipment available in the lab听allow complete studies of a material. The full list of tools of the SCML can be found on the 听website.
Materials Characterization
| Equipement | What for? | Specifications |
|---|---|---|
|
DSC 8000 (Perkin Elmer) |
Glass transition temperature , Fusion, Crystallization, Heat of reaction, Degree of cure |
Temperature: 25C to 700C听 (-80C with the cooling unit Intracooler II) Samples size: 15mg Modulation available |
|
Rheometer MCR 302 (Anton Parr) |
Viscosity, Shrinkage |
Temperature (with ETC): 25C to 600C Fixtures Available: Parallel plates 筛25mm & 筛40mm, torsion |
|
DSC Q100 (TA Instruments) |
Glass transition temperature听,听Fusion, Crystallization, Heat of reaction, Degree of cure |
Temperature: 25C to 725C (-70C with the cooling unit RCS90) Samples size: 15mg Modulation available |
|
DMA Q800 (TA Instruments) |
Loss and Storage Modulus behavior, Glass transition temperature听 |
Temperature: 25C to 600C听(-90C with the external liquid nitrogen tank) Clamps available: Dual & Single Cantilever, 3 pt bending, compression, film & fibre tension |
|
TMA Q400 (TA Instruments) |
Expansion Coefficient, Glass transition temperature听 |
Temperature: 25C to 700C (-70C with the cooling unit RCS90) Probes available: Penetration, MacroExpansion, Expansion |
|
TGA Q500 (TA Instruments) |
Degradation temperature |
Temperature: 25C to 1000C Samples size: up 100mg |
| Permeability fixture |
Transverse Permeability |
Room Temperature Sample: 筛3in |
| Microscopy |
Visual observation of samples characteristics (voids, phases, interfaces, particules distribution, sizing, etc...)听 |
Objectives x5鈥攛50 Mosaic creation available with the automatic stage |
听
Mechanical Testing
|
Equipement听听 |
What for? | Specifications |
|---|---|---|
| MTS 5kN | Tensile tests, 3 & 4 point-bending, Curved beam, Peel test, Iosipescu shear test, Compression听 |
Load Cell: 5kN, 500N Environmental Chamber available (Temperature) |
|
MTS 100kN |
Tensile tests, 3 & 4 point-bending, Compression听 |
Load Cell: 100kN Environmental Chamber available听(Temperature + Humidity) |
|
MTS 250kN |
Tensile tests, 3 & 4 point-bending, Compression, Sample molding |
Load Cell: 250kN |
听
Processing
|
Equipement听听 |
What for? |
Specifications |
|---|---|---|
|
Macrodyne Press |
Part Manufacturing, Sample molding |
Temperature: 25C to 250C (water cooling) 250 tons Different molds available Addition of heating cartridges to the mold or vacuum possible |
| Aon 3D Printer | Part Manufacturing |
Temperature: up to 200C听 Printing size :450 x 450 x 640 mm Conditioning cabinet available |
| Prusa i3 MK3S+ 3D Printer | Part Manufacturing |
Temperature: up to 300C Printing size : 25脳21脳21 cm Conditioning cabinet available |
| Blue M Oven - Big Chamber | Curing, Drying |
Temperature: 25 to 200C |
|
Blue M Oven - Small Chamber (*2) |
Curing, Drying |
Temperature: 25 to 200C 25in x 20in x 20in |
|
Secotom 50 |
Cutting |
Cutting capacity:听165 x 50 mm Rotational Speed: 300 - 5000 rpm Diamond cutting blade specific to materials |
听
For any inquiry or future project please contact lucie.riffard [at] mcgill.ca (Lucie Riffard).